Photovoltaics from Milliwatts to Gigawatts. Tim Bruton
that solar cells were a good option, but his experiments with commercial selenium cells of low efficiency were disappointing. He and Pearson knew each other, and Pearson offered Chapin his lithium‐doped ‘solar cell’. Chapin tested it and found it 2.3% efficient – an enormous improvement on selenium, justifying further investigations into silicon’s potential. The next step was to replace the lithium with phosphorus. A small amount of phosphorus was evaporated on to the p type silicon to make a shallow n type region. Initial results weren’t particularly good, but then Chapin applied a thin plastic layer to act as an antireflection coating (ARC) on the otherwise highly reflecting silicon surface. This gave the encouraging result of around 4% cell efficiency, which was good progress toward Chapin’s target of 5.7% for a viable power source. However, further progress was slow, and forming a good electrical contact proved to be an ongoing problem. A spur to further activity came from Bell’s competitor, RCA, which was developing an ‘atomic battery’ using a strontium 90 source to irradiate a silicon solar cell, although efficiencies were poor. The breakthrough came when Fuller, who had been experimenting with boron to give a p type silicon emitter which offered a new configuration, demonstrated that heating an n type silicon wafer for 5.5 hours at 1000 °C in a boron trichloride atmosphere under reduced pressure could produce a 0.25 μm‐deep diffusion with a resistivity of .001 Ω/cm [23]. This equated to 40 Ω per square sheet resistance emitter, which is a typical figure for later commercial silicon solar cells. Arsenic was used to dope the silicon base n type to 0.1 Ω/cm, and this was then cut into long narrow strips in accordance with the best previous cell results. The emitter was formed using the new boron diffusion process, with the emitter itself wrapping around the cell as shown in Figure 1.4. It was then partially removed on the rear to expose the n type base. Contacts were made by electroplating rhodium to the exposed base and emitter [24]; the relative ease in forming these contacts represented a significant advance. A polystyrene layer with refractive index 1.6 was used as the ARC. The solar cell efficiency was approximately 6% [25]. Chapin had proposed a theoretical limit of 22% efficiency for silicon, but had stated that practical limitations would result in its being lower in the real world. The spectral response of the cell is shown in Figure 1.5. It was proposed that 10 cells connected in series would be needed to provide the 1 W of power required to charge the batteries at a repeater station in a rural carrier telephone system [24].
Figure 1.4 Schematic of the first successful silicon solar cell
Figure 1.5 (A) Normalised spectral response of a p on n silicon solar cell. (B) Solar spectrum. (C) Relative integrated response [23]
Source: C.S. Fuller: US Patent 3015590, 2nd Jan. 1962 (filed 5th March 1954)
The 6% efficiency result met Chapin’s original target and gave the impetus for further improvement. By November 1954, an 8%‐efficiency cell had been produced with the same wraparound structure [26], and by May 1955, 11% efficiency was demonstrated [27]. It is interesting to note that this structure – an n type wafer with all of the contact metallisation on the rear – has a resonance with the current world‐record silicon solar cell (26.7% efficiency), based on an n type wafer with rear contacts, but with amorphous silicon providing the p side of the junction [28]. In their 1954 patent filing, the inventors stated that ‘Sunlight is the most common, most accessible, and most economical form of energy on the Earth’s surface’ [24]. This group at Bell Labs opened the door for practical exploitation of this rich energy source, although it was a further 20 years before its true potential began to be fully exploited.
1.2.3 Hiatus
While the Bell discovery was heralded as a great breakthrough, with the New York Times stating it ‘may mark the beginning of a new era, leading eventually to the realisation of one of mankind’s most cherished dreams – the harnessing of the almost limitless energy of the sun for the uses of civilisation’ [29] and the US News & World Report claiming ‘the (silicon) strips may provide more power than all the world’s coal, oil and uranium’ [30], the reality in 1954 was somewhat different. The cost of the high‐purity silicon needed to make viable solar cells was very high at $845/kg, resulting in an estimated cost of electricity of $144/kWh, compared to $23.7/kWh for dry cell batteries and less than $0.02/kWh for retail grid electricity [31]. Despite this disadvantage, Bell’s manufacturing subsidiary, Western Electric, took up commercialisation. One of the first applications was powering a remote telephone line in rural Georgia (USA). However, the introduction of silicon transistors for voice amplification with a very low power requirement made the application redundant and activity at Bell largely declined [31]. Western Electric licensed other companies to manufacture the silicon solar cells, one of which, National Fabricated Products, went as far as to assemble a range of demonstration products. But no market was forthcoming and National Fabricated Products was taken over by Hoffman Electronics in 1956. Hoffman provided prototypes for both the US Coast Guard and the US Forest Service, but no business resulted. The initial enthusiasm cooled to the extent that in 1957 it was reported that ‘Viewed in the light of the world’s power needs, these gadgets are toys’ [32].
1.2.4 The First Successful Market: Satellites
Although a terrestrial market was slow to materialise, Hoffman Electronics continued to do research to improve solar cell efficiency and reduce cost. By the end of 1957, it had demonstrated a 12.5% (1 cm2)‐efficient silicon cell [33]. The discoveries at Bell Laboratories did not pass unnoticed amongst the military, and the US Army Signal Corps visited the company to evaluate the technology and concluded that the only viable application was for the power supply of an artificial earth satellite, which was a top secret project at the time [34]. This view was shared by the US Air Force – but not by the US Navy, which was eventually awarded the satellite project, and which had decided that silicon solar cells were ‘unconventional and not fully established’ [34]. Interdepartmental rivalries also played a part [35]. Nonetheless, when President Eisenhower first announced the satellite programme publicly in 1955, the New York Times published a sketch showing solar cells providing the power. Intense lobbying was carried out, particularly by Dr Hans Ziegler of the Signal Corps Research and Development Laboratory (USARDL), assisted by a decision to simplify the satellite’s mission and lighten its payload. Eventually, it was agreed that both a dry cell battery power supply and a solar‐powered transmitter would be used. Solar cells were tested by attaching them to the nose cones of two high‐altitude rockets and were shown to survive the rigours of the launch and of the space environment.
The first launch in December 1957 of the Vanguard TV‐3 satellite, depicted in Figure 1.6, failed, but the satellite itself was recovered [36]. The Vanguard 1, identical to the TV‐3, was successfully launched on 17 March 1958, with the expectation that it would remain in orbit for 2000 years (although later recalculation lowered this to 240 years). It is the oldest artificial satellite still orbiting the earth. Its scientific purpose as part of the International Geophysical Year was to obtain geodetic measurements of the shape of the planet. As predicted, the battery‐powered transmitter stopped working in June 1958, while the solar‐powered one continued until May 1964, when the last signals were received in Quito, Ecuador. The satellite was a 16.5 cm aluminium sphere weighing 1.48 kg. A 10 mW 108 MHz telemetry transmitter was powered by a set of mercury batteries, while a 5 mW 108.03 MHz beacon transmitter was powered by solar cells mounted in six 5 × 5 cm arrays, which gave a nominal power of 1 W, equating to an efficiency of 10% at 28 °C [34]. The cells